锌块的阴极保护法是在保护钢铁设备上连接一种更易失去电子的金属或合金。例如：钢闸门的保护，有的就应用这种方法。它是一种比较更为活泼的金属，如锌等，连接在钢闸门上。这样，当发生电化腐蚀时，被腐蚀的是那种比铁更活泼的金属，而铁被保护了。通常在轮船的尾部和在船壳的水线以下部分，装上一定数量的锌块，来防止船壳等的腐蚀，就是应用的这种方法。 目前，电化学保护发出应用除海水或河道中钢铁设备的保护外，还应用于防止电缆、石油管道、地下设备和化工设备等的腐蚀WZ17184466
The cathodic protection of zinc blocks is to connect a metal or alloy that is more likely to lose electrons in the protection of steel equipment. For example: the protection of steel gates, and some use this method. It is a more active metal, such as zinc, which is attached to the steel gate. Thus, when galvanic corrosion occurs, the metal that is corroded is more active than iron, and the iron is protected. Usually at the stern of the ship and in the following part of the hull waterline, with a certain amount of zinc block, to prevent corrosion of the hull, this method is applied. At present, electrochemical protection has been applied to protect the cable, oil pipeline, underground equipment and chemical equipment
优质的船用锌阳极厂家立博
锌合金牺牲阳极在使用过程中须注意的问题： 
1. 抗蚀性差。当合金成分中杂质元素铅、镉、锡超过标准时，导致铸件老化而发生变形，表现为体积胀大，机械性能特别是塑性显著下降，时间长了甚至破裂。 
铅、锡、镉在锌合金中溶解度很小，因而集中于晶粒边界而成为阴极，富铝的固溶体成为阳极，在水蒸气（电解质）存在的条件下，促成晶间电化学腐蚀。压铸件因晶间腐蚀而老化。 
2. 时效作用 
锌合金牺牲阳极的组织主要由含Al和Cu的富锌固溶体和含Zn的富Al固溶体所组成，它们的溶解度随温度的下降而降低。但由于压铸件的凝固速度极快，因此到室温时，固溶体的溶解度是大大地饱和了。经过一定时间之后，这种过饱和现象会逐渐解除，而使铸件地形状和尺寸略起变化。 
3.锌合金阳极压铸件不宜在高温和低温（0℃以下）的工作环境下使用。锌合金在常温下有较好的机械性能。但在高温下抗拉强度和低温下冲击性能都显著下降。WZ17184466 
锌阳极的种类很多，有高纯锌，Zn-Al系合金，Zn-Sn系合金，Zn-Hg系合金，Zn-Al-Mn系合金，Zn-Al-Cd系合金等。我国以前基本上采用纯锌阳极，之后便主要采用三元锌合金，即Zn-Al-Cd系合金。